OK Autrod 16.95
A continous solid corrosion resisting chromium-nickel-manganese wire for welding of austenitic stainless alloys of 18% Cr, 8% Ni, 7% Mn types. OK Autrod 16.95 has a general corrosion resistance similar to that of the corresponding parent metal. The higher silicon content improves the welding properties, such as wetting. The product is a modified variant of ER307, basically with a higher Mn content to make the weld metal less sensitive to hot cracking. When used for joining dissimilar materials the corrosion resistance is of secondary importance. The alloy is used in a wide range of applications across the industry such as joining of austenitic, manganese, work hardenable steels as well as armourplate and heat resistant steels.
Teste Charpy
As Welded | |
Valor de impacto | 96 ft-lb |
Valor de impacto | 130 J |
Temperatura de prueba | 68 °F |
Temperatura de prueba | 20 °C |
Propiedades típicas de Tensión
Alargamiento | Condición | Límite de flujo | Resistencia a la tracción |
41 % | As Welded | 450 MPa (65 ksi) | 640 MPa (93 ksi) |
Depósito
Corriente | Tasa de Deposición | Diámetro | Tensión | Velocidad de Alimentación |
80-240 A | 1.5-6.0 kg/h (3.3-13. lb/h) | 1.0 mm (0.040 in.) | 15-28 V | 4.0-16.0 m/min (157-630 in./min) |
100-300 A | 1.6-7.5 kg/h (3.5-16. lb/h) | 1.2 mm (0.047 in.) | 15-29 V | 3.0-14.0 m/min (118-551 in./min) |
65-220 A | 1.1-5.4 kg/h (2.4-11. lb/h) | 0.9 mm (0.035 in.) | 15-28 V | 3.5-18.0 m/min (138-709 in./min) |
55-160 A | 1.0-4.1 kg/h (2.2-9.0 lb/h) | 0.8 mm (0.030 in.) | 15-24 V | 4.0-17.0 m/min (157-669 in./min) |
230-375 A | 5.2-8.6 kg/h (11.5-19. lb/h) | 1.6 mm (1/16 in.) | 23-31 V | 5.5-9.0 m/min (217-354 in./min) |
Clasificaciones
Wire Electrode |
EN ISO 14343-A : G 18 8 Mn SFA/AWS A5.9 : ER307 mod Werkstoffnummer : ~1.4370 |
Aprobaciones
Aprobaciones |
CE EN 13479 DB 43.039.10 NAKS/HAKC 1.2MM VdTÜV 05420 |
Las aprobaciones se basan en la ubicación de la planta de fabricación. Por favor, contáctese con ESAB para obtener más información. |
Características de los consumibles
tipo de aleación | Austenitic (18 % Cr - 8 % Ni - 7 % Mn) |
Gas de protección | M12, M13 (EN ISO 14175) |
Composición química
Typical Weld Metal Analysis % | ||||||||||||||
C | Cr | Cu | Mn | Mo | Ni | P | S | Si | ||||||
0.1 % | 18.5 % | 0.1 % | 6.5 % | 0.1 % | 8.5 % | 0.010 % | 0.020 % | 1 % | ||||||
Typical Wire Composition % | ||||||||||||||
0.08 % | 18.7 % | 0.10 % | 7.0 % | 0.20 % | 8.1 % | - | - | 0.9 % |
Cómo comprar OK Autrod 16.95
ESAB ofrece una amplia red de distribuidores presentes en todo el territorio nacional. Además, el apoyo y la atención que necesitan por el distribuidor de ESAB (SAE).
Para hacer sus compras más fácil, hemos elaborado una lista de las compras en línea. Mientras usted navega en nuestro sitio web, usted puede agregar cualquier producto a su lista. Justo a continuación, enviar la lista con sus datos y esperar a que el retorno de un representante ESAB. Para encontrar el distribuidor más cercano o SAE, por favor, utilice nuestro Localizador de distribuidores, disponible en todas las páginas del sitio. Cualquier pregunta, por favor contáctenos.