OK Autrod 316LSi
A continuous solid corrosion resisting chroumium-nickel-molybdenium wire for welding of austenitic stainless alloys of 18% Cr - 8% Ni and 18% Cr - 10% Ni - 3% Mo types. OK Autrod 316LSi has a good general corrosion resistance, in particularly the alloy has very good resistance against corrosion in acid and chlorinated environments. The alloy has a low carbon content which makes it particularly recommended where there is a risc of intergranular corrosion. The higher silicon content improves the welding properties, such as wetting. The alloy is widely used in the chemical and food processing industries as well as in ship building and various types of architectural structures.
Teste Charpy
| as welded | ||||
Propiedades típicas de Tensión
| Condición | As Welded | As Welded |
| Gas de protección | Tested at 350°C. | |
| Resistencia a la tracción | 560 MPa (81 ksi) | 440 MPa (64 ksi) |
| Límite de flujo | 400 MPa (58 ksi) | 340 MPa (49 ksi) |
| Alargamiento | 37 % | 26 % |
Parámetros de soldadura
| Diámetro del Alambre | ||||
| 0.6 mm (0.025 in.) | ||||
| 1.14 mm (0.045 in.) | ||||
Depósito
| Corriente | Tasa de Deposición | Diámetro | Tensión | Velocidad de Alimentación |
| 55-160 A | 1.0-4.1 kg/h (2.2-9.0 lb/h) | 0.8 mm (0.030 in.) | 12-24 V | 4.0-17.0 m/min (157-669 in./min) |
| 80-240 A | 1.5-6.0 kg/h (3.3-13. lb/h) | 1.0 mm (0.040 in.) | 15-28 V | 4.0-16.0 m/min (157-630 in./min) |
| 100-300 A | 1.6-7.5 kg/h (3.5-16. lb/h) | 1.2 mm (0.047 in.) | 15-29 V | 3.0-14.0 m/min (118-551 in./min) |
| 65-220 A | 1.1-5.4 kg/h (2.4-11. lb/h) | 0.9 mm (0.035 in.) | 15-28 V | 3.5-18.0 m/min (138-709 in./min) |
| 230-375 A | 5.2-8.6 kg/h (11.5-19. lb/h) | 1.6 mm (1/16 in.) | 23-31 V | 5.5-9.0 m/min (217-354 in./min) |
Clasificaciones
| Wire Electrode |
SFA/AWS A5.9 : ER316LSi Werkstoffnummer : ~1.4430 EN ISO 14343-A : G 19 12 3 L Si |
Aprobaciones
| Aprobaciones |
CE EN 13479 CWB ER316LSi DB 43.039.05 DNV-GL VL 316 L (M13) NAKS/HAKC 0.8-1.2 mm VdTÜV 04268 |
| Las aprobaciones se basan en la ubicación de la planta de fabricación. Por favor, contáctese con ESAB para obtener más información. |
Características de los consumibles
| tipo de aleación | Austenitic (with approx. 8 % ferrite) 19% Cr - 12% Ni - 3% Mo - Low C - High Si |
| Gas de protección | M12, M13 (EN ISO 14175) |
Composición química
| Typical Weld Metal Analysis % | ||||||||||||||
| C | Cr | Cu | Mn | Mo | Ni | P | S | Si | ||||||
| 0.02 % | 18.5 % | 0.1 % | 1.8 % | 2.7 % | 12 % | 0.015 % | 0.015 % | 0.8 % | ||||||
| Typical Wire Composition % | ||||||||||||||
| 0.01 % | 18.4 % | 0.12 % | 1.8 % | 2.60 % | 12.2 % | - | - | 0.9 % | ||||||
Cómo comprar OK Autrod 316LSi
ESAB ofrece una amplia red de distribuidores presentes en todo el territorio nacional. Además, el apoyo y la atención que necesitan por el distribuidor de ESAB (SAE).
Para hacer sus compras más fácil, hemos elaborado una lista de las compras en línea. Mientras usted navega en nuestro sitio web, usted puede agregar cualquier producto a su lista. Justo a continuación, enviar la lista con sus datos y esperar a que el retorno de un representante ESAB. Para encontrar el distribuidor más cercano o SAE, por favor, utilice nuestro Localizador de distribuidores, disponible en todas las páginas del sitio. Cualquier pregunta, por favor contáctenos.